The Townline Tunnel is an underwater tunnel in Welland , Ontario , Canada carrying Highway 58A as well as the Canadian Pacific Railway under the Welland Canal .
54-534: The Townline Tunnel is a two-cell reinforced concrete tunnel with a rectangular cross-section. The roof is a post-tensioned concrete slab. The tunnel was built as a part of the Welland By-Pass project. Its construction was relatively easy since, like the Main Street Tunnel , it was being built at the same time as the channel above it and a simple cut and cover method could be used. The tunnel provides
108-453: A major role in the evolution of concrete construction as a proven and studied science. Without Hyatt's work, more dangerous trial and error methods might have been depended on for the advancement in the technology. Joseph Monier , a 19th-century French gardener, was a pioneer in the development of structural, prefabricated and reinforced concrete, having been dissatisfied with the existing materials available for making durable flowerpots. He
162-419: A reduction in its durability. Corrosion and freeze/thaw cycles may damage poorly designed or constructed reinforced concrete. When rebar corrodes, the oxidation products ( rust ) expand and tends to flake, cracking the concrete and unbonding the rebar from the concrete. Typical mechanisms leading to durability problems are discussed below. Cracking of the concrete section is nearly impossible to prevent; however,
216-434: A sidewalk for pedestrians, two lanes for vehicular traffic, as well as room for three sets of tracks for rail vehicles. It was opened for automobiles on July 13, 1972, and the first train crossed the tunnel on January 31, 1973. The tunnel is 330 metres (1083 ft) long and 35 metres (115 ft) wide. The low grade required for trains makes necessary that each approach to the tunnel stretch be 4 km (2.5 miles ). There
270-418: A sinkhole within the road. The tunnel was closed to vehicular traffic to allow for repair. It re-opened April 22. Reinforced concrete Reinforced concrete , also called ferroconcrete , is a composite material in which concrete 's relatively low tensile strength and ductility are compensated for by the inclusion of reinforcement having higher tensile strength or ductility. The reinforcement
324-426: A well-chosen concrete mix will provide additional protection for many applications. Uncoated, low carbon/chromium rebar looks similar to standard carbon steel rebar due to its lack of a coating; its highly corrosion-resistant features are inherent in the steel microstructure. It can be identified by the unique ASTM specified mill marking on its smooth, dark charcoal finish. Epoxy-coated rebar can easily be identified by
378-556: Is a station on Line 10 of the Paris Métro . It is located in the 15th arrondissement . The station opened as Beaugrenelle on 13 July 1913 as part of the initial section of line 8 as its temporary southern terminus, and with Opéra as its northern terminus. The line was then extended to Porte d'Auteuil on 30 September that same year, becoming its new southern terminus. It was then named after Place Beaugrenelle (now known as Place Charles Michels). Beaugrenelle ("beautiful Grenelle")
432-658: Is a mixture of coarse (stone or brick chips) and fine (generally sand and/or crushed stone) aggregates with a paste of binder material (usually Portland cement ) and water. When cement is mixed with a small amount of water, it hydrates to form microscopic opaque crystal lattices encapsulating and locking the aggregate into a rigid shape. The aggregates used for making concrete should be free from harmful substances like organic impurities, silt, clay, lignite, etc. Typical concrete mixes have high resistance to compressive stresses (about 4,000 psi (28 MPa)); however, any appreciable tension ( e.g., due to bending ) will break
486-528: Is coating them with zinc phosphate . Zinc phosphate slowly reacts with calcium cations and the hydroxyl anions present in the cement pore water and forms a stable hydroxyapatite layer. Penetrating sealants typically must be applied some time after curing. Sealants include paint, plastic foams, films and aluminum foil , felts or fabric mats sealed with tar, and layers of bentonite clay, sometimes used to seal roadbeds. Corrosion inhibitors , such as calcium nitrite [Ca(NO 2 ) 2 ], can also be added to
540-495: Is located across the bay from San Francisco . Two years later, El Campanil survived the 1906 San Francisco earthquake without any damage, which helped build her reputation and launch her prolific career. The 1906 earthquake also changed the public's initial resistance to reinforced concrete as a building material, which had been criticized for its perceived dullness. In 1908, the San Francisco Board of Supervisors changed
594-541: Is one in which both the compressive and tensile zones reach yielding at the same imposed load on the beam, and the concrete will crush and the tensile steel will yield at the same time. This design criterion is however as risky as over-reinforced concrete, because failure is sudden as the concrete crushes at the same time of the tensile steel yields, which gives a very little warning of distress in tension failure. Steel-reinforced concrete moment-carrying elements should normally be designed to be under-reinforced so that users of
SECTION 10
#1732845044643648-428: Is one in which the concrete element is only reinforced near the tensile face and the reinforcement, called tension steel, is designed to resist the tension. A doubly reinforced beam is the section in which besides the tensile reinforcement the concrete element is also reinforced near the compressive face to help the concrete resist compression and take stresses. The latter reinforcement is called compression steel. When
702-430: Is one in which the tension capacity of the tension steel is greater than the combined compression capacity of the concrete and the compression steel (over-reinforced at tensile face). So the "over-reinforced concrete" beam fails by crushing of the compressive-zone concrete and before the tension zone steel yields, which does not provide any warning before failure as the failure is instantaneous. A balanced-reinforced beam
756-579: Is the theoretical failure point with a certain probability. It is stated under factored loads and factored resistances. Reinforced concrete structures are normally designed according to rules and regulations or recommendation of a code such as ACI-318, CEB, Eurocode 2 or the like. WSD, USD or LRFD methods are used in design of RC structural members. Analysis and design of RC members can be carried out by using linear or non-linear approaches. When applying safety factors, building codes normally propose linear approaches, but for some cases non-linear approaches. To see
810-446: Is transferred from the concrete to the bar interface so as to change the tensile stress in the reinforcing bar along its length. This load transfer is achieved by means of bond (anchorage) and is idealized as a continuous stress field that develops in the vicinity of the steel-concrete interface. The reasons that the two different material components concrete and steel can work together are as follows: (1) Reinforcement can be well bonded to
864-404: Is usually, though not necessarily, steel reinforcing bars (known as rebar ) and is usually embedded passively in the concrete before the concrete sets. However, post-tensioning is also employed as a technique to reinforce the concrete. In terms of volume used annually, it is one of the most common engineering materials. In corrosion engineering terms, when designed correctly, the alkalinity of
918-462: The tensile strength of concrete was improved by the reinforcing. Before the 1870s, the use of concrete construction, though dating back to the Roman Empire , and having been reintroduced in the early 19th century, was not yet a proven scientific technology. Ernest L. Ransome , an English-born engineer, was an early innovator of reinforced concrete techniques at the end of the 19th century. Using
972-697: The 1890s, Wayss and his firm greatly contributed to the advancement of Monier's system of reinforcing, established it as a well-developed scientific technology. One of the first skyscrapers made with reinforced concrete was the 16-story Ingalls Building in Cincinnati, constructed in 1904. The first reinforced concrete building in Southern California was the Laughlin Annex in downtown Los Angeles , constructed in 1905. In 1906, 16 building permits were reportedly issued for reinforced concrete buildings in
1026-578: The CPR Hamilton Subdivision and the CPR Brookfield Siding. Townline Tunnel is known locally as the "Stinky Tunnel" due to the strong odor of rotten eggs as one passes through it. The distinct smell of hydrogen sulfide that is sometimes present in the tunnel is created by dissolving layers of gypsum which are present in the bedrock of the area. Rain and snow falling on the approaches to the tunnel, as well as ground water flow, necessitate
1080-673: The City of Los Angeles, including the Temple Auditorium and 8-story Hayward Hotel. In 1906, a partial collapse of the Bixby Hotel in Long Beach killed 10 workers during construction when shoring was removed prematurely. That event spurred a scrutiny of concrete erection practices and building inspections. The structure was constructed of reinforced concrete frames with hollow clay tile ribbed flooring and hollow clay tile infill walls. That practice
1134-592: The English counties of Norfolk and Suffolk. In 1877, Thaddeus Hyatt , published a report entitled An Account of Some Experiments with Portland-Cement-Concrete Combined with Iron as a Building Material, with Reference to Economy of Metal in Construction and for Security against Fire in the Making of Roofs, Floors, and Walking Surfaces , in which he reported his experiments on the behaviour of reinforced concrete. His work played
SECTION 20
#17328450446431188-695: The actual available length is inadequate for full development, special anchorages must be provided, such as cogs or hooks or mechanical end plates. The same concept applies to lap splice length mentioned in the codes where splices (overlapping) provided between two adjacent bars in order to maintain the required continuity of stress in the splice zone. In wet and cold climates, reinforced concrete for roads, bridges, parking structures and other structures that may be exposed to deicing salt may benefit from use of corrosion-resistant reinforcement such as uncoated, low carbon/chromium (micro composite), epoxy-coated, hot dip galvanized or stainless steel rebar. Good design and
1242-461: The actual bond stress varies along the length of a bar anchored in a zone of tension, current international codes of specifications use the concept of development length rather than bond stress. The main requirement for safety against bond failure is to provide a sufficient extension of the length of the bar beyond the point where the steel is required to develop its yield stress and this length must be at least equal to its development length. However, if
1296-472: The behavior of the final structure under working loads. In the United States , the most common methods of doing this are known as pre-tensioning and post-tensioning . For a strong, ductile and durable construction the reinforcement needs to have the following properties at least: François Coignet used iron-reinforced concrete as a technique for constructing building structures. In 1853, Coignet built
1350-543: The chief reasons for the failure of reinforcement bars in concrete. The relative cross-sectional area of steel required for typical reinforced concrete is usually quite small and varies from 1% for most beams and slabs to 6% for some columns. Reinforcing bars are normally round in cross-section and vary in diameter. Reinforced concrete structures sometimes have provisions such as ventilated hollow cores to control their moisture & humidity. Distribution of concrete (in spite of reinforcement) strength characteristics along
1404-732: The city's building codes to allow wider use of reinforced concrete. In 1906, the National Association of Cement Users (NACU) published Standard No. 1 and, in 1910, the Standard Building Regulations for the Use of Reinforced Concrete . Many different types of structures and components of structures can be built using reinforced concrete elements including slabs , walls , beams , columns , foundations , frames and more. Reinforced concrete can be classified as precast or cast-in-place concrete . Designing and implementing
1458-422: The compression zone of a concrete is inadequate to resist the compressive moment (positive moment), extra reinforcement has to be provided if the architect limits the dimensions of the section. An under-reinforced beam is one in which the tension capacity of the tensile reinforcement is smaller than the combined compression capacity of the concrete and the compression steel (under-reinforced at tensile face). When
1512-521: The concrete protects the steel rebar from corrosion . Reinforcing schemes are generally designed to resist tensile stresses in particular regions of the concrete that might cause unacceptable cracking and/or structural failure. Modern reinforced concrete can contain varied reinforcing materials made of steel, polymers or alternate composite material in conjunction with rebar or not. Reinforced concrete may also be permanently stressed (concrete in compression, reinforcement in tension), so as to improve
1566-541: The concrete resists compression and reinforcement " rebar " resists tension can be made into almost any shape and size for the construction industry. Three physical characteristics give reinforced concrete its special properties: As a rule of thumb, only to give an idea on orders of magnitude, steel is protected at pH above ~11 but starts to corrode below ~10 depending on steel characteristics and local physico-chemical conditions when concrete becomes carbonated. Carbonation of concrete along with chloride ingress are amongst
1620-412: The concrete roof and floors in the two-story house he was constructing. His positioning of the reinforcement demonstrated that, unlike his predecessors, he had knowledge of tensile stresses. Between 1869 and 1870, Henry Eton would design, and Messrs W & T Phillips of London construct the wrought iron reinforced Homersfield Bridge bridge, with a 50' (15.25 meter) span, over the river Waveney, between
1674-416: The concrete, thus they can jointly resist external loads and deform. (2) The thermal expansion coefficients of concrete and steel are so close ( 1.0 × 10 to 1.5 × 10 for concrete and 1.2 × 10 for steel) that the thermal stress-induced damage to the bond between the two components can be prevented. (3) Concrete can protect the embedded steel from corrosion and high-temperature induced softening. Because
Townline Tunnel - Misplaced Pages Continue
1728-507: The concrete, which occurs when compressive stresses exceed its strength, by yielding or failure of the rebar when bending or shear stresses exceed the strength of the reinforcement, or by bond failure between the concrete and the rebar. Carbonation, or neutralisation, is a chemical reaction between carbon dioxide in the air and calcium hydroxide and hydrated calcium silicate in the concrete. Rue Charles Michels Charles Michels ( French pronunciation: [ʃaʁl miʃɛl] )
1782-403: The cross-section of vertical reinforced concrete elements is inhomogeneous. The reinforcement in a RC structure, such as a steel bar, has to undergo the same strain or deformation as the surrounding concrete in order to prevent discontinuity, slip or separation of the two materials under load. Maintaining composite action requires transfer of load between the concrete and steel. The direct stress
1836-403: The examples of a non-linear numerical simulation and calculation visit the references: Prestressing concrete is a technique that greatly increases the load-bearing strength of concrete beams. The reinforcing steel in the bottom part of the beam, which will be subjected to tensile forces when in service, is placed in tension before the concrete is poured around it. Once the concrete has hardened,
1890-557: The first concrete buildings constructed in the United States was a private home designed by William Ward , completed in 1876. The home was particularly designed to be fireproof. G. A. Wayss was a German civil engineer and a pioneer of the iron and steel concrete construction. In 1879, Wayss bought the German rights to Monier's patents and, in 1884, his firm, Wayss & Freytag , made the first commercial use of reinforced concrete. Up until
1944-506: The first iron reinforced concrete structure, a four-story house at 72 rue Charles Michels in the suburbs of Paris. Coignet's descriptions of reinforcing concrete suggests that he did not do it for means of adding strength to the concrete but for keeping walls in monolithic construction from overturning. The, 1872–1873, Pippen building in Brooklyn stands as a testament to his technique. In 1854, English builder William B. Wilkinson reinforced
1998-645: The knowledge of reinforced concrete developed during the previous 50 years, Ransome improved nearly all the styles and techniques of the earlier inventors of reinforced concrete. Ransome's key innovation was to twist the reinforcing steel bar, thereby improving its bond with the concrete. Gaining increasing fame from his concrete constructed buildings, Ransome was able to build two of the first reinforced concrete bridges in North America. One of his bridges still stands on Shelter Island in New Yorks East End, One of
2052-811: The light green color of its epoxy coating. Hot dip galvanized rebar may be bright or dull gray depending on length of exposure, and stainless rebar exhibits a typical white metallic sheen that is readily distinguishable from carbon steel reinforcing bar. Reference ASTM standard specifications A1035/A1035M Standard Specification for Deformed and Plain Low-carbon, Chromium, Steel Bars for Concrete Reinforcement, A767 Standard Specification for Hot Dip Galvanized Reinforcing Bars, A775 Standard Specification for Epoxy Coated Steel Reinforcing Bars and A955 Standard Specification for Deformed and Plain Stainless Bars for Concrete Reinforcement. Another, cheaper way of protecting rebars
2106-438: The microscopic rigid lattice, resulting in cracking and separation of the concrete. For this reason, typical non-reinforced concrete must be well supported to prevent the development of tension. If a material with high strength in tension, such as steel , is placed in concrete, then the composite material, reinforced concrete, resists not only compression but also bending and other direct tensile actions. A composite section where
2160-656: The most efficient floor system is key to creating optimal building structures. Small changes in the design of a floor system can have significant impact on material costs, construction schedule, ultimate strength, operating costs, occupancy levels and end use of a building. Without reinforcement, constructing modern structures with concrete material would not be possible. When reinforced concrete elements are used in construction, these reinforced concrete elements exhibit basic behavior when subjected to external loads . Reinforced concrete elements may be subject to tension , compression , bending , shear , and/or torsion . Concrete
2214-423: The operation of a pumping system to prevent flooding. Water is pumped via pipes located under the road and discharged into the canal. In February 1985, excessive runoff during a winter thaw caused flooding in the tunnel which closed the route to both rail and vehicular traffic. In late March, 2010, a routine inspection of the concrete pipes through which the water is pumped revealed erosion which threatened to cause
Townline Tunnel - Misplaced Pages Continue
2268-448: The passivation of steel at the anodic oxidation sites. Nitrite is a much more active corrosion inhibitor than nitrate , which is a less powerful oxidizer of the divalent iron. A beam bends under bending moment , resulting in a small curvature. At the outer face (tensile face) of the curvature the concrete experiences tensile stress, while at the inner face (compressive face) it experiences compressive stress. A singly reinforced beam
2322-433: The reinforced concrete element is subject to increasing bending moment, the tension steel yields while the concrete does not reach its ultimate failure condition. As the tension steel yields and stretches, an "under-reinforced" concrete also yields in a ductile manner, exhibiting a large deformation and warning before its ultimate failure. In this case the yield stress of the steel governs the design. An over-reinforced beam
2376-581: The size and location of cracks can be limited and controlled by appropriate reinforcement, control joints, curing methodology and concrete mix design. Cracking can allow moisture to penetrate and corrode the reinforcement. This is a serviceability failure in limit state design . Cracking is normally the result of an inadequate quantity of rebar, or rebar spaced at too great a distance. The concrete cracks either under excess loading, or due to internal effects such as early thermal shrinkage while it cures. Ultimate failure leading to collapse can be caused by crushing
2430-558: The station as well as the nearby Place Beaugrenelle were renamed Charles Michels and Place Charles Michels respectively, in honour of Charles Michels (1903–1941), a trade unionist, communist militant, and deputy of the 15th arrondissement in Paris . He was held hostage and shot during the Occupation by the Nazis in retaliation for the assassination of Karl Hotz , amongst 44 other people. Hence,
2484-552: The station was used by 4,601,730 passengers, making it the 93rd busiest of the Métro network out of 302 stations. In 2020, the station was used by 2,198,392 passengers amidst the COVID-19 pandemic , making it the 194th busiest of the Métro network out of 108 stations. In 2021, the station was used by 3,079,569 passengers, making it the 102nd busiest of the Métro network out of 305 stations. The station has 2 accesses: The station has
2538-650: The station, along with 7 other stations, were renamed after the Second World War to honour the resistance fighters who had died for France. The other stations were: Colonel Fabien , Corentin Cariou , Corentin Celton , Guy Môquet , Jacques Bonsergent , Marx Dormoy , and Trinité - d'Estienne d'Orves . As part of the "Renouveau du métro" programme by the RATP , the station's platforms were renovated and modernised in 2009. In 2019,
2592-468: The structure will receive warning of impending collapse. The characteristic strength is the strength of a material where less than 5% of the specimen shows lower strength. The design strength or nominal strength is the strength of a material, including a material-safety factor. The value of the safety factor generally ranges from 0.75 to 0.85 in Permissible stress design . The ultimate limit state
2646-454: The tension on the reinforcing steel is released, placing a built-in compressive force on the concrete. When loads are applied, the reinforcing steel takes on more stress and the compressive force in the concrete is reduced, but does not become a tensile force. Since the concrete is always under compression, it is less subject to cracking and failure. Reinforced concrete can fail due to inadequate strength, leading to mechanical failure, or due to
2700-403: The water mix before pouring concrete. Generally, 1–2 wt. % of [Ca(NO 2 ) 2 ] with respect to cement weight is needed to prevent corrosion of the rebars. The nitrite anion is a mild oxidizer that oxidizes the soluble and mobile ferrous ions (Fe ) present at the surface of the corroding steel and causes them to precipitate as an insoluble ferric hydroxide (Fe(OH) 3 ). This causes
2754-469: Was a name given by property developers in the Grenelle district during its urbanisation. On 27 July 1937, the section of line 8 between La Motte-Picquet–Grenelle and Porte d'Auteuil , including Beaugrenelle , was transferred to line 10 during the reconfiguration of lines 8, 10, and the old line 14 . On 29 July 1937, line 10 was extended from Duroc to La Motte-Picquet–Grenelle . On 14 July 1945, both
SECTION 50
#17328450446432808-404: Was granted a patent for reinforcing concrete flowerpots by means of mixing a wire mesh and a mortar shell. In 1877, Monier was granted another patent for a more advanced technique of reinforcing concrete columns and girders, using iron rods placed in a grid pattern. Though Monier undoubtedly knew that reinforcing concrete would improve its inner cohesion, it is not clear whether he even knew how much
2862-498: Was removed about 13,750,000 cubic meters (18,000,000 cubic yards) of material and construction of three viaducts on each side of the canal. As well, a solid earth plug had to be put into the Welland Recreational Waterway (the old alignment of the canal), cutting it in two ( satellite photo ). The construction cost was $ 40 million. The middle rail line was removed in the 1990s and the two remaining tracks now serve as
2916-422: Was strongly questioned by experts and recommendations for "pure" concrete construction were made, using reinforced concrete for the floors and walls as well as the frames. In April 1904, Julia Morgan , an American architect and engineer, who pioneered the aesthetic use of reinforced concrete, completed her first reinforced concrete structure, El Campanil, a 72-foot (22 m) bell tower at Mills College , which